TH series double component coating
Product description: TH series of two-component coating has good adhesion, chemical resistance, wear resistance, and has the characteristics of fast drying, high leveling, plump apperance;
Main components: Hydroxy acrylic resin, pigment, auxiliaries, organic solvents
Applicable products: It is suitable for household appliances, electric appliances, 3C electronics, etc.
Applicable base materials: ABS﹑PC﹑ABS+PC﹑PPS﹑PET﹑TPU﹑nylon and metal etc.
Environmental conformance: Meet the requirements of ROHS. Can also be designed the products according to customer requirements to meet Reach/PAHS/ halogen-free etc.
Important explanation: According to customer requirements, our TH series have multi formula can be selected for different base materials with a single or multiple coating.
Workpiece inspection --> degreasing and dedusting --> Confirmation of the furnace temperature --> painting --> inspection --> packaging for good products
Construction conditions:
Name |
TH series double component coating |
Blending water |
W-TH series blending water |
Hardener |
Supporting hardener |
Blending percentage |
Depending on the product system |
Construction viscosity |
9-11S(NK#2/25±1℃) |
Spray gun caliber |
1.0-1.5mm |
Spray gun pressure |
3-5Kg/cm2 |
Spray distance |
15-20cm |
Thickness of dry film |
15-25μm |
Construction environment |
temperature: 5-40℃/ humidity: 40-80% |
Dry condition |
room temperature×5~10mins |
Baking condition |
room temperature×5~10mins |
性能:
Test project |
Test Method |
Test result |
|
Adhesion |
Cross-cut test, 3M600 tape stripping test |
5B |
|
Hardness |
MITSUBISHI UNI diurnal pencil, carry weight 500gf, ∠45° |
≥HB |
|
Alcohol resistance |
99.7% alcohol, carry weight 500gf, frequency:40times(come and go)/mins |
≥100times |
|
Bottom materials invisiable |
|||
耐RCA磨耗性 |
Norman 7-IBB RCA paper tape tester,carry weight 175gf |
≥30times |
|
Heat and humidity resistance |
40℃×90%RH×120H |
No obvious change in the surface of the paint film |
|
Thermal cycling |
(-20℃×2H-room temperature×1H-60℃×2H-room temperature×1H) |
No obvious change in the surface of the paint film |
|
10 times cycling |
1.Please stir well before use;
2.Please refer to "construction technology instruction" to remove oil, degrease and dust before use.
3.Please use the suitable strainer screen for filtration.
4.For performance testing, please bake at 65±5℃×2H condition or let it stay in room temperature for 168 hours, then process after cooling for 30 minutes.
5.Due to the different types and forming conditions of the rubber, please confirm it fully before using the coating to ensure its adaptability.
6.When the humidity is too high, besides adding the necessary anti white solvent, it is suggested that put into the bake road or oven to prevent blushing.
7.The coating should not be too thin and too thick, too thin to protect the film, it is easy to get bad adhension and bubble etc if it is too thick.
8.7. When the hardener is opened, please seal it in time so as not to react with the moisture in the air.
9.The proportion of the main paint and the hardener must be weighed accurately.
10.The main paint and hardener were mixed well, must be finished it within 4 hours under room temperature, otherwise easy to get gelling, The higher environment temperature, the shorter time can be used.
11.The gun of the spraying double liquid coating must be cleaned every hour in order to prevent the clogging. At the same time, the pipe and the gun must be washed with the washing gun solvent.
12.According to the different types of products, it is necessary to pack the packing after complete drying. If there is a re-coating requirement, please inform us in advance, and we will give professional guidance.
Warm reminder
Quality guarantee period: The expiration date is half a year with sealed。
Storage conditions: Stored in a cool, dry, special chemical reservoir, away from the fire source。