UV curable coatings
Product description: UV series UV curable coatings have the characteristics of fast curing, high smooth, endurable for water cook, high chemical resistance, high wear resistance and high hardness ect.
Main components: Oligomer, Active diluent, Initiator, Auxiliary, organic solvent.
Applicable products: Applied to 3C electronic products, TV sets, cosmetics etc.
Applicable base materials: ABS、PC、ABS+PC、PMMA、PP、TPU、Metal and other plastic products; if match the appropriate primer also suitable for glass, pet and nylon etc.
Environmental conformance: Meet the requirements of ROHS.
Workpiece inspection --> degreasing and dedusting --> Confirmation of the furnace temperature --> painting --> inspection --> packaging for good products
Construction conditions:
Name |
UV curable coatings |
Blending water |
WU-V series blending water
|
Blending percentage |
paint: blending water= 1: 0.3~1 |
Construction viscosity |
9-11S(NK#2/25±1℃) |
Spray gun caliber |
1.0-1.5mm |
Spray gun pressure |
3-5Kg/cm2 |
Spray distance |
15-20cm |
Thickness of dry film |
10-30μm |
Construction environment |
temperature: 5-40℃/ humidity: 40-80% |
Dry condition |
40-60℃×3~5mins |
能量 |
400-1000MJ/CM2 |
Performance(Below data represent the mobile phone with UV coating performance)
Test project |
Test Method |
Test result |
|
Adhesion |
Cross-cut test, 3M600 tape stripping test |
5B |
|
Hardness |
MITSUBISHI UNI diurnal pencil, carry weight 500gf, ∠45° |
≥H |
|
Alcohol resistance |
99.7% alcohol, carry weight 500gf, frequency:40times(come and go)/mins |
≥1000times |
|
Bottom materials invisiable |
|||
Resistance to RCA abrasion |
Norman RCA paper tape tester, carry weight 175gf, continuous friction paint film |
≥1000times |
|
Surface |
|||
Resistance to water cook abrasion |
Constant temperature water bath, to cook with 85℃×1H or 100℃×0.5H water |
nothing happens in surface |
|
Resistance to aging |
XHS-LH-02A UV aging experiment box, irradiation for 72hours |
No cracking, no tarnishing |
|
△E<3(white bottom) |
|||
Vibration and wear resistance |
Roster vibration and wear-resistant instrument frequency:1.7 test: 1H |
wear area:longth dia. <2mm |
|
equipment weight: 150g |
width dia. <2mm |
||
Resistance to cosmetics |
Constant temperature constant humidity box: 55±2℃ relative humidity: 93%, put inside for 48H |
nothing happens on surface |
|
Test separately with handcream/ sunscreen(SPF=30)/ edible oil/ liquid foundation |
painting for second time: 4-5B |
||
Heat and humidity resistance |
40℃×90%RH×120H |
No obvious change in the surface of the paint film |
|
Heat and humidity resistance Bending experiment |
Cylindrical shaft bending test instrument |
Paint film without shedding |
|
<12mm, bending angle: 180° |
|||
Thermal cycling |
(-40℃×1H-room temperature×1H-75℃×2H-room temperature×1H) |
Paint film without shedding |
|
20 times cycling |
1.Please stir well before use;
2.Please carry out pre treatment according to actual needs, such as ultrasonic cleaning, phosphating, sand blasting, etc.
3.Please use 500 mesh filter net for filtering;
4.The viscosity of primer should not be too high, otherwise it is easy to get rough surface like the orange peel and surface should not be too thin, otherwise it will easy to get pinholes, especially the coarse particle pearlescent silver powder varnish should not be too thick, otherwise it will crack and the interlayer is densely undesirable.
5.The bottom coating must be fully dry,otherwise it will cross the paint with the bottom and surface then influence on the lustre of the surface.
6.UV must be pre baked before light curing, otherwise whitening and other phenomena will appear.
7.The spraying and curing environment should be clean, and make sure any water can not remain in the air compressor.
8.Storage in a whole one, construction sites can not be exposed directly in the sunlight.
Warm reminder
Quality guarantee period: The expiration date is half a year with sealed。
Storage conditions: Stored in a cool, dry, special chemical reservoir, away from the fire source。