TK series hardware lacquer
Product description: TK series hardware lacquer have the characteristics of high gloss, high leveling, endurable for water cook, acid resistance and alkali resistance, high wear resistance, suitable for electrostatic spraying and suitable for wet collision wet spraying.
Main components: Thermosetting acrylic resin, amino resin, pigment, auxiliaries, organic solvents
Applicable products: It is used in living appliances, cabinet, lighting etc.
Applicable base materials: Stainless steel, aluminum alloy, zinc alloy, water electroplating, galvanized sheet and so on.
Environmental conformance: Meet the requirements of ROHS. Can also be designed the products according to customer requirements to meet Reach/PAHS/ halogen-free etc.
Workpiece inspection --> degreasing and dedusting --> Confirmation of the furnace temperature --> painting --> inspection --> packaging for good products
Construction conditions:
Name |
TK series hardware lacquer |
Blending water |
W-TK series blending water |
Blending percentage |
paint: blending water= 1: 0.5~1 |
Construction viscosity |
9-13S(NK#2/25±1℃) |
Spray gun caliber |
1.0-1.5mm |
Spray gun pressure |
3-5Kg/cm2 |
Spray distance |
15-20cm |
Thickness of dry film |
20±2μm |
Construction environment |
temperature: 5-40℃/ humidity: 40-80% |
Dry condition |
room temperature×5~10mins |
Baking condition |
150℃×30mins |
性能:
Test project |
Test Method |
Test result |
|
Adhesion |
Cross-cut test, 3M600 tape stripping test |
5B |
|
Hardness |
MITSUBISHI UNI diurnal pencil, carry weight 500gf, ∠45° |
≥2H |
|
Alcohol resistance |
99.7% alcohol, carry weight 500gf, frequency:40times(come and go)/mins |
≥100times |
|
The bottom of the paint film can not be visiable, and can not be decolorization |
|||
Butanone resistant |
carry weight 500gf frequency:40times(come and go)/mins |
≥50times |
|
The bottom of the paint film can not be visiable, and can not be decolorization |
|||
Acid resistance test |
Soak the gauze with the solution (50% acetic acid: 50% lactic acid=1:1), then stick to the surface of the paint film, and let it stay uner room temperature for 1 hour, observe the surface of the film after rinsing with clear water. |
No abnormality |
|
Salt-fog test |
Continuous spray with nature salt-fog for 160 hours corrosion≤1mm |
No abnormality |
|
Resistance to water cook abrasion |
Put half of the sample into the boiling water and continuously heated with electromagnetic furnace for 2 hours, the sample should be standed for 30mins after test , after that, observe the surface and test the adhesion. |
No abnormality |
|
Heat and humidity resistance |
60℃×95%RH×240H |
No obvious change in the surface of the paint film |
|
Thermal cycling |
(-20℃×2H-room temperature×1H-60℃×2H-room temperature×1H) |
No obvious change in the surface of the paint film |
|
10 times cycling |
1﹑Please stir well before use;
2﹑Please carry out pre treatment according to the actual needs, such as ultrasonic cleaning, phosphating, sand blasting, etc;
3﹑Please use the suitable strainer screen for filtration;
4﹑The coating should not be too thin and too thick, too thin to protect the film, it is easy to get bubble if it is too thick;
Warm reminder
Quality guarantee period: The expiration date is half a year with sealed。
Storage conditions: Stored in a cool, dry, special chemical reservoir, away from the fire source。