TAB series of high alcohol resistant&high wear resistant single component coatings
Product description: TA series has good adhesion and excellent construction.
Main components: Thermoplastic acrylic resins, pigments, auxiliaries, organic solvents.
Applicable products: It is suitable for household appliances, life electric appliance, 3C electronic products, etc.
Applicable base materials: ABS﹑PS﹑HIPS﹑PC etc.
Environmental conformance: Meet the requirements of ROHS. Can also be designed the products according to customer requirements to meet Reach/PAHS/ halogen-free /EN71-3 etc.
Workpiece inspection --> degreasing and dedusting --> Confirmation of the furnace temperature --> painting --> inspection --> packaging for good products
Construction conditions:
Name |
TAB series of high alcohol resistant&high wear resistant single component coatings |
Blending water |
W-TA series blending water |
Blending percentage |
paint: blending water= 1:1.5-2.5(Depending on the customers construction technology and work piece) |
Construction viscosity |
9-11S(NK#2/25±1℃) |
Spray gun caliber |
1.0-1.5mm |
Spray gun pressure |
3-5Kg/cm2 |
Spray distance |
15-20cm |
Thickness of dry film |
8-13μm |
Construction environment |
temperature: 5-40℃/ humidity: 40-80% |
Dry condition |
room temperature×5~10mins |
Baking condition |
65±5℃×30 |
性能:
Test project |
Test Method |
Test result |
|
Adhesion |
Cross-cut test, 3M600 tape stripping test |
5B |
|
Hardness |
MITSUBISHI UNI diurnal pencil, carry weight 500gf, ∠45° |
≥HB |
|
Alcohol resistance |
99.7% alcohol, carry weight 500gf, frequency:40times(come and go)/mins |
≥200 times |
|
Bottom materials invisiable |
|||
Heat and humidity resistance |
40℃×90%RH×120H |
No obvious change in the surface of the paint film |
|
Thermal cycling |
(-20℃×2H-room temperature×1H-60℃×2H-room temperature×1H) |
No obvious change in the surface of the paint film |
|
10 times cycling |
1﹑Please stir well before use;
2﹑Please refer to "construction technology instruction" to remove oil, degrease and dust before use;
3﹑Please use the suitable strainer screen for filtration;
4﹑For performance testing, please bake at 65±5℃×2H condition and process after cooling for 30 minutes;
5﹑Due to the different types and forming conditions of the rubber, please confirm it fully before using the coating to ensure its adaptability;
6﹑When the humidity is too high, besides adding the necessary anti white solvent, it is suggested that put into the bake road or oven to prevent blushing;
7﹑The coating should not be too thin and too thick, too thin to protect the film, it is easy to affect the chemical resistance test when coating again if it is too thick;
Warm reminder
Quality guarantee period: The expiration date is half a year with sealed。
Storage conditions: Stored in a cool, dry, special chemical reservoir, away from the fire source。